Electromagnetic Properties of Flaky Metal Magnetic Powder Coated by Coupling Agent
- Received Date: 2006-07-17
- Rev Recd Date: 2006-11-30
- Publish Date: 2008-04-15
-
Key words:
- metal magnetic powder /
- permittivity /
- silane coupling agent /
- surface coating
Abstract: The surface of flaky metal magnetic powders was coated by silane coupling agent. The appearance, structure and phase constitute of powders before and after treatment were characterized by SEM and RA-IR. And the powders were randomly dispersed in paraffin at a weight ratio of 5:1 for microwave electromagnetic parameters test and comparison in the frequency range of 2~18 GHz. The results show that a high resistivity film is formed on the powders surface by chemical bonding, and the real and imaginary parts of complex permittivity of sample decrease 9 in average but corresponding complex permeability decreases slightly. The coatings with thicknesses of 1 mm give a microwave absorption of 8 dB with a band width of 8.2 GHz and microwave absorption of the coated flaky metal magnetic powders is improved.
Citation: | XIE Jian-liang, LU Chuan-lin, DENG Long-jiang, CHEN liang. Electromagnetic Properties of Flaky Metal Magnetic Powder Coated by Coupling Agent[J]. Journal of University of Electronic Science and Technology of China, 2008, 37(2): 293-296. |